High refractive index glass composition

ABSTRACT

A glass composition including SiO 2  in an amount from 30.0 to 40.0% by weight, Al 2 O 3  in an amount from 15.0 to 23.0% by weight, B 2 O 3  in an amount from 0.0 to 15.0% by weight, K 2 O in an amount from 0.0 to 5.0% by weight, La 2 O 3  in an amount from 0.0 to 30.0% by weight, Li 2 O in an amount from 0.0 to 3.0% by weight, Na 2 O in an amount from 0.0 to 4.0% by weight, Nb 2 O 5  in an amount from 0.0 to 10.0% by weight, TiO 2  in an amount from 0.0 to 7.5% by weight, WO 3  in an amount from 0.0 to 10.0% by weight, Y 2 O 3  in an amount from 15.0 to 35.0% by weight, and RO (one or more of MgO, CaO, SrO, and BaO) in an amount from 0.0 to 7.5% by weight is provided. Glass fibers formed from the composition have a refractive index between 1.55 and 1.69.

RELATED APPLICATIONS

This application claims the benefit of provisional U.S. patent application Ser. No. 61/394,166 filed on Oct. 18, 2010 for HIGH REFRACTIVE INDEX GLASS COMPOSITION, the entire disclosure of which is fully incorporated herein by reference.

TECHNICAL FIELD

The present invention relates generally to a glass composition, and more particularly, to a glass composition for forming high refractive index glass fibers. The glass fibers may be used to reinforce plastics and form a composite having a high refractive index. These high refractive index composites may then be used in applications where high strength and transparency are required.

BACKGROUND

Glass fibers are manufactured from various raw materials combined in specific proportions to yield a desired chemical composition. This collection of materials is commonly termed a “glass batch.” To form glass fibers, typically the glass batch is melted in a melter or melting apparatus, the molten glass is drawn into filaments through a bushing or orifice plate, and a sizing composition containing lubricants, coupling agents and film-forming binder resins is applied to the filaments. After the sizing is applied, the fibers may be gathered into one or more strands and wound into a package or, alternatively, the fibers may be chopped while wet and collected. The collected chopped strands may then be dried and cured to form dry chopped fibers or they can be packaged in their wet condition as wet chopped fibers. The fibers, in turn, may be used to reinforce plastics and various other structural and non-structural products.

The composition of the glass batch and the glass manufactured from it are generally expressed in terms of percentages of the components and are mainly expressed as oxides. Compounds such as SiO₂, Al₂O₃, CaO, MgO, B₂O₃, La₂O, Nb₂O₅, Ta₂O₅, ZrO₂, ₂O₃, Li₂O, Na₂O, GdO₃, BaO, SrO, ZnO, ZrO₂, P₂O₅, GeO₂, WO₃, Fe₂O₃, fluorine, and SO₃ may be used to form a glass batch. Numerous types of glasses may be produced from varying the amounts of these oxides, or eliminating some of the oxides in the glass batch. Normal reinforcement glasses such as R-glass, E-glass, S-glass, A-glass, C-glass, and ECR-glass may be formed from certain combinations of the oxides. In addition, optical glasses having a desired refractive index can be produced by choosing oxides for the glass batch. The glass composition controls the forming and product properties of the glass. Characteristics of glass compositions include the raw material cost and environmental impact.

High refractive index glasses and use thereof in optical lens applications are known in the art. However, conventional optical glass fibers are unable to be formed by conventional fiberizing techniques because they lack sufficient viscosity above their crystallization temperature to be formed into fibers. Thus, although high refractive index glasses exist, there remains a need in the art for glass compositions that possess a high refractive index, an Abbe number and a coefficient of thermal expansion that is appropriate for the reinforcement of high refractive index plastics, and a viscosity above the liquidus temperature that is sufficiently high to permit the formation of fibers using conventional fiber forming techniques.

SUMMARY OF THE INVENTION

The general inventive concepts include a composition that includes SiO₂ in an amount from 30.0 to 40.0% by weight, Al₂O₃ in an amount from 15.0 to 23.0% by weight, B₂O₃ in an amount from 0.0 to 15.0% by weight, K₂O in an amount from 0.0 to 5.0% by weight, La₂O₃ in an amount from 0.0 to 30.0% by weight, Li₂O in an amount from 0.0 to 3.0% by weight, Na₂O in an amount from 0.0 to 4.0% by weight, Nb₂O₅ in an amount from 0.0 to 10.0% by weight, TiO₂ in an amount from 0.0 to 7.5% by weight, WO₃ in an amount from 0.0 to 10.0% by weight, Y₂O₃ in an amount from 15.0 to 35.0% by weight, and RO in an amount from 0.0 to 7.5% by weight, where RO is one or more of MgO, CaO, SrO, and BaO. The phrase “% by weight”, as used herein, is intended to be defined as the percent by weight of the total composition.

In some exemplary embodiments, the composition also contains trace quantities of other components or impurities that are not intentionally added. Also, in some exemplary embodiments, the glass composition is free or substantially free of fluorine and lead.

In some exemplary embodiments, glass fibers formed from the composition have a refractive index between 1.55 and 1.69, an Abbe number less than about 65, and a coefficient of thermal expansion (CTE) less than about 66×10⁻⁷ cm/cm. Further, the glass composition and fibers produced therefrom possess a CTE and an Abbe number that may be suitable for reinforcing high refractive index plastics.

In some exemplary embodiments, the glass composition possesses a viscosity above the liquidus temperature that is sufficiently high to permit the glass fibers to be formed using conventional fiber forming techniques, such as, for example, a platinum-lined melter.

In some exemplary embodiments, a reinforced composite is formed from a matrix material and a plurality of fibers formed from the composition described. The matrix material may be any suitable thermoplastic or thermoset resin known to those of skill in the art, and includes thermoplastics and thermoset resins such as polyesters, polypropylene, polyamide, polyethylene terephthalate, polybutylene, polysulfone, polyethersulfone, polyether imide, polyarylate, epoxy resins, unsaturated polyesters, phenolics, vinylesters, and elastomers. The polymer resins can be used alone or in combination to form the final composite product.

In some exemplary embodiments, glass fibers formed from the inventive compositions have a liquidus temperature no greater than about 1531° C., a log 3 temperature less than about 1443° C., and a ΔT up to about 77° C.

In yet other exemplary embodiments, glass fibers formed from the inventive composition have a refractive index between about 1.55 and about 1.69, preferably from about 1.55 to about 1.65.

In further exemplary embodiments, glass fibers formed from the inventive composition have an Abbe number less than about 65, preferably less than about 60, and a coefficient of thermal expansion less than about 66×10″⁷ cm/cm, preferably less than about 55×10⁻⁷ cm/cm.

In some exemplary embodiments, the difference between the forming temperature and the crystallization temperature is from about −170° C. to about 77° C.

The foregoing and other objects, features, and advantages of the invention will appear more fully hereinafter from a consideration of the detailed description that follows.

DETAILED DESCRIPTION

Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which the invention belongs. Although any methods and materials similar or equivalent to those described herein can be used in the practice or testing of the present invention, the preferred methods and materials are described herein. All references cited herein, including published or corresponding U.S. or foreign patent applications, issued U.S. or foreign patents, and any other references, are each incorporated by reference in their entireties, including all data, tables, figures, and text presented in the cited references. The terms “composition” and “formulation” may be used interchangeably herein. Additionally, the phrase “inventive glass composition” and “glass composition” may be interchangeably used.

The general inventive concepts relate to a glass composition used to form continuous glass fibers that may be used to reinforce high refractive index polymer matrices and form transparent or translucent composite products. In addition, the glass composition has a viscosity that is sufficiently above the liquidus temperature to permit the glass fibers to be fowled using currently available fiber forming techniques, such as, for example, a platinum-lined melter.

In some exemplary embodiments, the inventive glass composition includes the following components in the weight percent ranges given in Table 1. As used herein, the terms “weight percent” and “percent by weight” may be used interchangeably and are meant to denote the weight percent (or percent by weight) based on the total composition.

TABLE 1 % by Chemical weight SiO₂ 30.0-40.0 Al₂O₃ 15.0-23.0 B₂O₃  0.0-15.0 K₂O 0.0-5.0 La₂O₃  0.0-30.0 Li₂O 0.0-3.0 Na₂O 0.0-4.0 Nb₂O₅  0.0-10.0 TiO₂ 0.0-7.5 WO₃  0.0-10.0 Y₂O₃ 15.0-35.0 MgO + CaO + SrO + BaO 0.0-7.5

In some exemplary embodiments, the glass composition includes the components set forth in Table 2.

TABLE 2 % by Chemical weight SiO₂ 30.0-33.0 Al₂O₃ 16.0-22.0 B₂O₃  5.0-10.0 La₂O₃ 10.0-26.0 Nb₂O₅ 0.0-2.0 TiO₂ 0.0-1.5 Y₂O₃ 17.0-33.0

Further, it is to be appreciated that impurities or trace materials may be present in the glass composition without adversely affecting the glasses or the fibers. These impurities may enter the glass as raw material impurities or may be products formed by the chemical reaction of the molten glass with furnace components. Non-limiting examples of trace materials include Fe₂O₃, Cr₂O₃, CeO₂, Pr₂O₃, Nd₂O₃, Pm₂O₃, Sm₂O₃, Eu₂O₃, Gd₂O₃, Tb₂O₃, Dy₂O₃, Ho₂O₃, Er₂O₃, Tm₂O₃, Yb₂O₃ and Lu₂O₃, all of which are present in their oxide forms, and fluorine and chlorine.

The glass fibers produced from the inventive composition may have a refractive index between about 1.55 and about 1.69, an Abbe number less than about 65, and a coefficient of thermal expansion less than about 66×10⁻⁷ cm/cm. In some exemplary embodiments, the glass fibers have a refractive index between about 1.55 and about 1.65, an Abbe number less than about 55, and a coefficient of thermal expansion less than about 52×10⁻⁷ cm/cm. The difference between the forming temperature and the crystallization temperature is from about −170° C. to about 77° C. Also, the viscosity as a function of temperature of the glass is such that glass fibers formed from the inventive composition may be formed in conventional platinum-lined melters (e.g., paramelters).

In the glass composition, SiO₂, Y₂O₃, and B₂O₃ provide a glass network for the fiber. The SiO₂ also plays a role in the chemical and thermal stability of the formed glass fiber. La₂O, Nb₂O₅, and Y₂O₃ are effective for increasing the refractive index of the glass fiber. TiO₂ is optionally added to adjust the refractive index and Abbe number. Al₂O₃ may be added to improve the chemical durability of the glass fiber. In some exemplary embodiments, the glass composition is free or substantially free of fluorine and lead, although either may be added at levels less than about 1% without adversely affecting the glass properties.

The fiberizing properties of the glass composition of the present invention include the fiberizing temperature, the liquidus temperature, and ΔT. The fiberizing temperature is defined as the temperature that corresponds to a viscosity of about 1000 Poise. Lowering the fiberizing temperature may reduce the production cost of the glass fibers because it allows for a longer bushing life and reduced energy usage. For example, at a lower fiberizing temperature, a bushing operates at a cooler temperature and does not quickly “sag”. Sag is a phenomenon that occurs in bushings that are held at an elevated temperature for extended periods of time. Thus, by lowering the fiberizing temperature, the sag rate of the bushing may be reduced and the bushing life can be increased. In the present invention, the glass composition has a fiberizing temperature (i.e., log 3 temperature) that is less than about 1443° C. In exemplary embodiments, the log 3 temperature is from about 1081° C. to about 1443° C.

The liquidus temperature is defined as the highest temperature at which equilibrium exists between liquid glass and its primary crystalline phase. At all temperatures above the liquidus temperature, the glass is free from crystals in its primary phase. At temperatures below the liquidus temperature, crystals may form. Additionally, the liquidus temperature is the greatest temperature at which devitrification can occur upon cooling the glass melt. At all temperatures above the liquidus temperature, the glass is completely molten. In exemplary embodiments, the liquidus temperature of the inventive composition may range from about 1169° C. to about 1531° C.

A third fiberizing property is “ΔT”, which is defined as the difference between the fiberizing temperature (i.e., log 3 temperature) and the liquidus temperature. If the ΔT is too small, the molten glass may crystallize within the fiberizing apparatus and cause a break in the manufacturing process. Additionally, glasses with small or negative ΔT values may be formed utilizing methods that are not commonly employed when forming reinforcement fibers. For instance, discontinuous fibers may be generated by blowing gas or steam through a molten stream of glass. These discontinuous fibers require additional processing (such as carding or needle felting) to form them into suitable reinforcement fibers. Alternatively, continuous fibers can be formed from glasses having small or negative ΔT values by elevating the forming temperature well above the log 3 temperature. The temperature chosen needs to be above the liquidus temperature to prevent devitrification. The inventive composition may have a ΔT up to about 77° C., in exemplary embodiments, from about −170° C. to about 77° C.

In general, glass fibers according to the present invention may be formed by obtaining the raw materials or ingredients and mixing or blending the components in a conventional manner in the appropriate quantities to give the desired weight percentages of the final composition. For example, the components may be obtained from suitable ingredients or raw materials including, but not limited to, sand or pyrophyllite for SiO₂, kaolin, alumina or pyrophyllite for Al₂O₃, lithium carbonate or spodumene for Li₂O and sodium feldspar, sodium carbonate or sodium sulfate for Na₂O, potassium feldspar or potassium carbonate for K₂O, Lanthanum oxide or Rare Earth Oxide blends for La₂O₃, rutile or ilmenite for TiO₂, and the remainder of the composition is supplied by refined oxides of Nb₂O₅, WO₃, or Y₂O₃. Glass cullet can also be used to supply one or more of the needed oxides.

The mixed batch is then melted in a platinum-lined melter, and the resulting molten glass is passed into bushings (e.g., platinum-alloy based bushings). The operating temperatures of the glass in the furnace and bushing are selected to appropriately adjust the viscosity of the glass, and may be maintained using suitable methods such as control devices. Preferably, the temperature at the front end or bottom of the melter is automatically controlled to reduce or eliminate devitrification. The molten glass is then pulled (drawn) through holes or orifices in the bottom or tip plate of the bushing to form glass fibers. The streams of molten glass flowing through the bushing orifices are attenuated to filaments by winding a strand formed of a plurality of individual filaments on a forming tube mounted on a rotatable collet of a winding machine or chopped at an adaptive speed.

The fibers may be further processed in a conventional manner suitable for the intended application. For instance, the continuous glass fibers may be sized with a sizing composition known to those of skill in the art. The sizing composition is in no way restricted, and may be any sizing composition suitable for application to glass fibers. The sized fibers may be used for reinforcing substrates, such as a variety of plastics, where the end product is desired to have a high refractive index. Such applications include, but are not limited to, the reinforcement of high refractive index plastics that have high strength and temperature resistance useful for laboratory equipment or a protective layer for flexible LCD screens. In this regard, the present invention also includes a composite material having a high refractive index that includes the inventive glass fibers, as described above, in combination with a hardenable matrix material. The matrix material may be any suitable thermoplastic or thermoset resin known to those of skill in the art, such as, but not limited to thermoplastics and thermoset resins such as polyesters, polypropylene, polyamide, polyethylene terephthalate, polybutylene, polysulfone, polyethersulfone, polyether imide, polyarylate, epoxy resins, unsaturated polyesters, phenolics, vinylesters, and elastomers. The polymer resins can be used alone or in combination to form the final composite product.

Having generally described this invention, a further understanding can be obtained by reference to certain specific examples illustrated below which are provided for purposes of illustration only and are not intended to be all inclusive or limiting unless otherwise specified.

EXAMPLES Example 1 High Refractive Glass Compositions

Glass compositions according to the present invention were made by mixing reagent grade chemicals in proportioned amounts to achieve a final glass composition with the oxide weight percentages set forth in Tables 3-15. The raw materials were melted in a platinum crucible in an electrically heated furnace at a temperature of 1650° C. for 3 hours. The Abbe number was calculated from the refractive index of the glass measured at three wavelengths, 589.2 nm (d), 486.1 nm (F), and 656.3 nm (C). The Abbe number, V, was then calculated from the following equation:

$V = \frac{n_{d} - 1}{n_{F} - n_{c}}$

The coefficient of thermal expansion was measured by linear extension according to ASTM E228-06. The refractive index was measured using temperature controlled standardized immersion oils according to ASTM E1967-98. The forming viscosity (i.e., the temperature that corresponds to a viscosity of about 1000 Poise) was measured using a rotating cylinder method (ASTM C965). The liquidus temperature was measured by exposing glass to a temperature gradient in a platinum-alloy boat for 16 hours (ASTM C829). Density was measured by the Archimedes method (ASTM C693-93). The modulus was measured indirectly by measuring the speed of sound in a fiber with a known density.

TABLE 3 Ex. 1 Ex. 2 Ex. 3 Ex. 4 Ex. 5 Ex. 6 Ex. 7 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 20.76 20.76 20.76 20.76 19.67 19.67 19.67 B₂O₃ 5.00 0.00 0.00 0.00 10.00 0.00 0.00 MgO + CaO + 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 0.00 5.00 0.00 0.00 0.00 10.00 0.00 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 0.00 0.00 0.00 5.00 0.00 0.00 0.00 SiO₂ 39.76 39.76 39.76 39.76 37.67 37.67 37.67 TiO₂ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 WO₃ 0.00 0.00 5.00 0.00 0.00 0.00 10.00 Y₂O₃ 34.48 34.48 34.48 34.48 32.67 32.67 32.67 Property Abbe Number 56.1 58.5 58 (FU) Refractive 1.6190 1.6475 1.6405 1.6503 1.6060 1.6596 1.6500 Index (BA) CTE 46 46.6 46.8 50.3 39.4 47 (cm × 10⁻⁷/cm) Log 3 1268 1386 1302 1245 1385 Temp (° C.) Liquidus Temp 1302 1418 1439 1458 1264 1413 (° C.) ΔT (° C.) −34 −32 −137 −28

TABLE 4 Ex. 8 Ex. 9 Ex. 10 Ex. 11 Ex. 12 Ex. 13 Ex. 14 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 19.67 19.34 17.26 22.26 16.01 16.01 16.01 B₂O₃ 0.00 5.00 10.00 8.75 15.00 8.75 8.75 MgO + CaO + 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 0.00 6.50 11.00 9.75 9.75 16.00 9.75 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 10.00 0.00 0.00 0.00 0.00 0.00 0.00 SiO₂ 37.67 37.04 33.06 31.82 31.82 31.82 38.07 TiO₂ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 32.67 32.12 28.67 27.42 27.42 27.42 27.42 Property Abbe Number 57.5 52.5 52.4 53.8 43.8 (FU) Refractive 1.6684 1.6340 1.6330 1.6346 1.6200 1.6516 1.6190 Index (BA) CTE 43.1 52 53.4 43.3 49 43.7 43.5 (cm × 10⁻⁷/cm) Log 3 1443 1279 1190 1207 1161 1185 1255 Temp (° C.) Liquidus Temp 1531 1303 1194 1311 1199 1257 1233 (° C.) ΔT (° C.) −88 −24 −4 −103 −38 −72 22

TABLE 5 Ex. 15 Ex. 16 Ex. 17 Ex. 18 Ex. 19 Ex. 20 Ex. 21 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 16.01 16.76 16.76 16.76 16.26 16.26 16.26 B₂O₃ 8.75 9.50 9.50 9.50 9.00 9.00 9.00 MgO + CaO + 0.00 2.50 0.00 0.00 5.00 0.00 0.00 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 9.75 10.50 10.50 10.50 10.00 10.00 10.00 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 0.00 0.00 0.00 2.50 0.00 0.00 5.00 SiO₂ 31.82 32.57 32.57 32.57 32.07 32.07 32.07 TiO₂ 0.00 0.00 2.50 0.00 0.00 5.00 0.00 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 33.67 28.17 28.17 28.17 27.67 27.67 27.67 Property Abbe Number 49.7 48.5 53.6 63.8 57.6 46.9 49.9 (FU) Refractive Index 1.6516 1.6347 1.6480 1.6440 1.6399 1.6620 1.6530 (BA) CTE 43.8 42.5 49.7 50.4 50.5 46.8 44.5 (cm × 10⁻⁷/cm) Log 3 1184 1191 1179 1184 1193 1174 1209 Temp (° C.) Liquidus Temp 1284 1256 1223 1225 1265 1252 1371 (° C.) ΔT (° C.) −100 −64 −44 −41 −72 −77 −162

TABLE 6 Ex. 22 Ex. 23 Ex. 24 Ex. 25 Ex. 26 Ex. 27 Ex. 28 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 15.76 15.76 15.76 16.26 16.26 16.26 15.76 B₂O₃ 8.50 8.50 8.50 9.00 9.00 9.00 8.50 MgO + CaO + 7.50 0.00 0.00 2.50 2.50 0.00 2.50 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 9.50 9.50 9.50 10.00 10.00 10.00 9.50 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 0.00 0.00 7.50 0.00 2.50 2.50 2.50 SiO₂ 31.57 31.57 31.57 32.07 32.07 32.07 31.57 TiO₂ 0.00 7.50 0.00 2.50 0.00 2.50 2.50 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 27.17 27.17 27.17 27.67 27.67 27.67 27.17 Property Abbe Number 53 46 49.3 (FU) Refractive Index 1.6402 1.6750 1.6620 1.6507 1.6454 (BA) CTE 53.1 49 40.2 48.3 50.9 47.2 45.7 (cm × 10⁻⁷/cm) Log 3 1189 1164 1179 1186 1173 1172 Temp (° C.) Liquidus Temp 1299 1222 1397 1213 1216 1232 1208 (° C.) ΔT (° C.) −110 −58 −34 −31 −59 −37

TABLE 7 Ex. 29 Ex. 30 Ex. 31 Ex. 32 Ex. 33 Ex. 34 Ex. 35 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 17.00 16.74 16.91 16.57 16.83 16.40 21.00 B₂O₃ 9.85 9.70 9.80 9.60 9.75 9.50 5.07 MgO + CaO + SrO + 0.00 0.00 0.00 0.00 0.00 0.00 0.00 BaO K₂O 0.00 0.00 0.00 0.00 2.50 5.00 0.00 La₂O₃ 10.83 10.67 10.78 10.56 10.73 10.45 28.93 Li₂O 1.50 3.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 2.00 4.00 0.00 0.00 0.00 Nb₂O₅ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SiO₂ 32.58 32.08 32.41 31.75 32.24 31.41 30.00 TiO₂ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 28.24 27.81 28.10 27.52 27.95 27.24 15.00 Property Abbe Number (FU) Refractive Index (BA) CTE 53.7 66.1 54.1 66.1 56.9 65.8 51.7 (cm × 10⁻⁷/cm) Log 3 1130 1081 1176 1164 1189 1184 1206 Temp (° C.) Liquidus Temp 1228 1251 1273 1300 1251 1288 1226 (° C.) ΔT (° C.) −98 −170 −97 −136 −61 −103 −20

TABLE 8 Ex. 36 Ex. 37 Ex. 38 Ex. 39 Ex. 40 Ex. 41 Ex. 42 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 16.95 16.64 16.32 20.07 19.13 18.20 19.00 B₂O₃ 9.69 9.38 9.06 6.30 7.54 8.77 6.00 MgO + CaO + 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 10.69 10.38 10.06 24.45 19.96 15.48 23.00 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SiO₂ 32.76 32.45 32.13 30.77 31.53 32.30 32.00 TiO₂ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 29.92 31.17 32.42 18.42 21.84 25.26 20.00 Property Abbe Number (FU) Refractive Index 1.6535 (BA) CTE 50.8 49.4 49.7 51.4 49.3 48.2 (cm × 10⁻⁷/cm) Log 3 1199 1178 1179 1201 1184 1196 1200 Temp (° C.) Liquidus Temp 1213 1258 1218 1204 1199 1169 1246 (° C.) ΔT (° C.) −14 −80 −39 −3 −16 27 −46

TABLE 9 Ex. 43 Ex. 44 Ex. 45 Ex. 46 Ex. 47 Ex. 48 Ex. 49 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 19.37 19.00 19.49 19.00 19.39 19.00 19.41 B₂O₃ 6.36 6.00 6.36 6.00 6.14 7.00 6.99 MgO + CaO + 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 23.26 24.00 23.71 26.00 25.31 23.00 23.30 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 0.17 1.50 1.07 0.00 0.11 0.00 0.24 SiO₂ 31.54 32.00 31.71 32.00 31.69 31.50 31.36 TiO₂ 0.11 0.00 0.19 0.00 0.16 1.50 1.04 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 19.19 17.50 17.47 17.00 17.20 18.00 17.65 Property Abbe Number 54.08 (FU) Refractive 1.6529 1.6533 1.6533 1.6523 1.652 1.657 1.6553 Index (BA) CTE 44.0 (cm × 10⁻⁷/cm) Log 3 1189 1201 1195 1201 1202 1184 1190 Temp (° C.) Liquidus Temp 1209 1210 1229 1201 1212 1205 1174 (° C.) ΔT (° C.) −20 −9 −34 0 −10 −21 16

TABLE 10 Ex. 50 Ex. 51 Ex. 52 Ex. 53 Ex. 54 Ex. 55 Ex. 56 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 19.00 19.42 19.00 19.37 19.00 19.38 20.50 B₂O₃ 7.50 7.40 8.00 7.65 8.00 7.62 8.00 MgO + CaO + 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 25.00 24.61 23.00 23.21 23.00 23.33 23.00 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 0.00 0.27 0.00 0.15 1.50 1.21 0.00 SiO₂ 30.50 30.48 30.00 30.21 30.50 30.49 30.00 TiO₂ 0.00 0.23 0.00 0.18 0.00 0.24 1.50 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 18.00 17.61 20.00 19.23 18.00 17.73 17.00 Property Abbe Number (FU) Refractive 1.6517 1.6534 1.6531 1.6532 1.6527 1.6515 1.6529 Index (BA) CTE (cm × 10⁻⁷/cm) Log 3 1190 1186 1179 1181 1183 1178 1180 Temp (° C.) Liquidus Temp 1207 1203 1178 1212 1216 1184 1276 (° C.) ΔT (° C.) −17 −17 1 −31 −33 −7 −96

TABLE 11 Ex. 57 Ex. 58 Ex. 59 Ex. 60 Ex. 61 Ex. 62 Ex. 63 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 20.32 21.00 21.09 21.00 20.98 21.00 20.85 B₂O₃ 7.56 5.00 5.48 6.00 6.15 7.00 6.91 MgO + CaO + 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 23.35 23.00 23.23 24.50 24.04 23.00 23.20 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 0.24 0.50 0.43 0.00 0.24 2.00 1.28 SiO₂ 30.27 32.00 31.73 31.00 31.05 30.00 30.42 TiO₂ 0.99 0.00 0.19 0.50 0.31 0.00 0.12 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 17.27 18.50 17.85 17.00 17.24 17.00 17.20 Property Abbe Number (FU) Refractive 1.6556 1.6541 1.6528 1.6525 1.6506 1.6551 1.6535 Index (BA) CTE (cm × 10⁻⁷/cm) Log 3 1187 1215 1212 1200 1204 1182 1199 Temp (° C.) Liquidus Temp 1252 1291 1280 1272 1268 1277 1272 (° C.) ΔT (° C.) −65 −76 −68 −71 −64 −95 −73

TABLE 12 Ex. 64 Ex. 65 Ex. 66 Ex. 67 Ex. 68 Ex. 69 Ex. 70 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 21.50 21.06 20.64 20.08 18.46 17.46 16.46 B₂O₃ 6.50 6.67 6.74 6.72 6.99 6.99 6.99 MgO + CaO + 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 23.00 23.23 23.32 23.69 23.30 23.30 23.30 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 0.00 0.16 0.63 0.51 0.24 0.24 0.24 SiO₂ 30.00 30.38 30.65 30.99 31.36 31.36 31.36 TiO₂ 0.00 0.15 0.33 0.36 2.00 3.00 4.00 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 19.00 18.35 17.68 17.65 17.65 17.65 17.65 Property Abbe Number (FU) Refractive 1.6532 1.6520 1.6526 1.6531 1.6562 1.662 1.6697 Index (BA) CTE (cm × 10⁻⁷/cm) Log 3 1194 1200 1188 1189 1181 1172 1163 Temp (° C.) Liquidus Temp 1283 1261 1256 1245 1188 1141 1133 (° C.) ΔT (° C.) −89 −61 −68 −56 −7 31 30

TABLE 13 Ex. 71 Ex. 72 Ex. 73 Ex. 74 Ex. 75 Ex. 76 Ex. 77 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt.) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 15.46 19.41 19.41 19.41 19.41 19.41 19.41 B₂O₃ 6.99 6.03 5.03 4.03 3.03 6.99 6.99 MgO + CaO + 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 23.30 23.30 23.30 23.30 23.30 23.30 23.30 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 0.24 0.24 0.24 0.24 0.24 0.24 0.24 SiO₂ 31.36 31.36 31.36 31.36 31.36 30.40 29.40 TiO₂ 5.00 2.00 3.00 4.00 5.00 2.00 3.00 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 17.65 17.65 17.65 17.65 17.65 17.65 17.65 Property Abbe Number (FU) Refractive 1.6754 1.6597 1.668 1.6774 1.6857 1.6605 1.6688 Index (BA) CTE (cm × 10⁻⁷/cm) Log 3 1152 1179 1180 1183 1183 1164 1158 Temp (° C.) Liquidus Temp 1181 1234 1249 1261 1272 1217 1231 (° C.) ΔT (° C.) −29 −56 −69 −78 −88 −53 −72

TABLE 14 Ex. 78 Ex. 79 Ex. 80 Ex. 81 Ex. 82 Ex. 83 Ex. 84 (% by (% by (% by (% by (% by (% by (% by wt.) wt.) wt.) wt.) wt.) wt.) wt.) Chemical Al₂O₃ 19.41 19.41 19.25 18.76 18.26 17.77 17.52 B₂O₃ 6.99 6.99 6.92 6.92 6.92 6.92 7.20 MgO + CaO + 0.00 0.00 0.00 0.00 0.00 0.00 0.00 SrO + BaO K₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 La₂O₃ 23.30 23.30 23.06 23.06 23.06 23.06 23.28 Li₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Na₂O 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Nb₂O₅ 0.24 0.24 0.24 0.24 0.24 0.24 0.00 SiO₂ 28.40 27.40 31.08 30.58 30.09 29.59 31.58 TiO₂ 4.00 5.00 1.98 2.97 3.96 4.95 2.82 WO₃ 0.00 0.00 0.00 0.00 0.00 0.00 0.00 Y₂O₃ 17.65 17.65 17.47 17.47 17.47 17.47 17.61 Property Abbe Number (FU) Refractive 1.677 1.686 1.6566 1.6634 1.6718 1.6792 1.6560 Index (BA) CTE (cm × 10⁻⁷/cm) Log 3 1142 1135 1166 1164 1157 1146 1181 Temp (° C.) Liquidus Temp 1234 1249 1217 1209 1187 1179 1104 (° C.) ΔT (° C.) −92 −113 −51 −45 −29 −33 77

TABLE 15 Ex. 85 Ex. 86 (% by (% by wt.) wt.) Chemical Al₂O₃ 17.23 17.42 B₂O₃ 7.26 6.86 MgO + CaO + 0.00 0.00 SrO + BaO K₂O 0.00 0.00 La₂O₃ 23.34 23.42 Li₂O 0.00 0.00 Na₂O 0.00 0.00 Nb₂O₅ 0.00 0.00 SiO₂ 31.69 31.25 TiO₂ 2.84 3.27 WO₃ 0.00 0.00 Y₂O₃ 17.65 17.78 Property Abbe Number (FU) Refractive 1.6597 1.6633 Index (BA) CTE (cm × 10⁻⁷/cm) Log 3 1178 1172 Temp (° C.) Liquidus Temp 1163 1148 (° C.) ΔT (° C.) 15 24

Looking at Tables 3-15, it can be concluded that the glass compositions of Examples 1-86 have a very high refractive index in comparison with commercially available continuous fiber products (e.g., the refractive index for S2 glass is 1.52, E-glass is about 1.58 to 1.62 and ECR glass is 1.58) with forming temperatures and ΔT values that allow these glasses to be manufactured by known platinum-lined furnace melting techniques.

The invention of this application has been described above both generically and with regard to specific embodiments. Although the invention has been set forth in what is believed to be the preferred embodiments, a wide variety of alternatives known to those of skill in the art can be selected within the generic disclosure. The invention is not otherwise limited, except for the recitation of the claims set forth below. 

Having thus described the invention, what is claimed is:
 1. A composition for preparing glass fibers having a high refractive index comprising: SiO₂ in an amount from 30.0 to 40.0% by weight; Al₂O₃ in an amount from 15.0 to 23.0% by weight; Y₂O₃ in an amount from 15.0 to 35.0% by weight; B₂O₃ in an amount from 0.0 to 15.0% by weight; K₂O in an amount from 0.0 to 5.0% by weight; La₂O₃ in an amount from 0.0 to 30.0% by weight; Li₂O in an amount from 0.0 to 3.0% by weight; Na₂O in an amount from 0.0 to 4.0% by weight; Nb₂O₅ in an amount from 0.0 to 10.0% by weight; TiO₂ in an amount from 0.0 to 7.5% by weight; WO₃ in an amount from 0.0 to 10.0% by weight; and RO in an amount from 0.0 to 7.5% by weight, wherein RO is one or more of MgO, CaO, SrO, and BaO.
 2. The composition of claim 1, wherein said composition has a ΔT up to about 77° C.
 3. The composition of claim 1, wherein said composition has a ΔT from about −170° C. to about 77° C.
 4. The composition of claim 1, wherein said composition has a log 3 temperature that is less than about 1443° C.
 5. The composition of claim 1, wherein said composition has a liquidus temperature greater than about 1531° C.
 6. The composition of claim 1, wherein said composition is substantially free of fluorine and lead.
 7. The composition of claim 1, wherein said composition comprises: SiO₂ in an amount from 30.0 to 33.0% by weight; Al₂O₃ in an amount from 16.0 to 22.0% by weight; Y₂O₃ in an amount from 17.0 to 33% by weight; B₂O₃ in an amount from 5.0 to 10.0% by weight; La₂O₃ in an amount from 10.0 to 26.0% by weight; Nb₂O₅ in an amount from 0.0 to 2.0% by weight; and TiO₂ in an amount from 0.0 to 1.5% by weight.
 8. A continuous high refractive index glass fiber produced from a composition comprising: SiO₂ in an amount from 30.0 to 40.0% by weight; Al₂O₃ in an amount from 15.0 to 23.0% by weight; Y₂O₃ in an amount from 15.0 to 35.0% by weight; B₂O₃ in an amount from 0.0 to 15.0% by weight; K₂O in an amount from 0.0 to 5.0% by weight; La₂O₃ in an amount from 0.0 to 30.0% by weight; Li₂O in an amount from 0.0 to 3.0% by weight; Na₂O in an amount from 0.0 to 4.0% by weight; Nb₂O₅ in an amount from 0.0 to 10.0% by weight; TiO₂ in an amount from 0.0 to 7.5% by weight; WO₃ in an amount from 0.0 to 10.0% by weight; and RO in an amount from 0.0 to 7.5% by weight, wherein RO is one or more of MgO, CaO, SrO, and BaO.
 9. The glass fiber of claim 8, wherein said glass fiber has a refractive index between about 1.55 and about 1.69.
 10. The glass fiber of claim 9, wherein said composition is substantially free of fluorine and lead.
 11. The glass fiber of claim 8, wherein said glass fiber has an Abbe number less than about 65 and a coefficient of thermal expansion less than about 66×10⁻⁷ cm/cm.
 12. A reinforced composite product comprising: a polymer matrix; and a plurality of glass fibers, said glass fibers being produced from a composition comprising: SiO₂ in an amount from 30.0 to 40.0% by weight; Al₂O₃ in an amount from 15.0 to 23.0% by weight; Y₂O₃ in an amount from 15.0 to 35.0% by weight; B₂O₃ in an amount from 0.0 to 15.0% by weight; K₂O in an amount from 0.0 to 5.0% by weight; La₂O₃ in an amount from 0.0 to 30.0% by weight; Li₂O in an amount from 0.0 to 3.0% by weight; Na₂O in an amount from 0.0 to 4.0% by weight; Nb₂O₅ in an amount from 0.0 to 10.0% by weight; TiO₂ in an amount from 0.0 to 7.5% by weight; WO₃ in an amount from 0.0 to 10.0% by weight; and RO in an amount from 0.0 to 7.5% by weight, wherein RO is one or more of MgO, CaO, SrO, and BaO.
 13. The composite product of claim 12, wherein said glass fibers have a refractive index between about 1.55 and about 1.69 and an Abbe number less than about
 65. 14. The composite product of claim 13, wherein said glass fibers have a coefficient of thermal expansion less than about 66×10⁻⁷ cm/cm.
 15. The composite product of claim 13, wherein said refractive index is between about 1.55 and about 1.65 and said Abbe number is less than about
 60. 16. The composite product of claim 12, wherein said composition comprises: SiO₂ in an amount from 30.0 to 33.0% by weight; Al₂O₃ in an amount from 16.0 to 22.0% by weight; Y₂O₃ in an amount from 17.0 to 33% by weight; B₂O₃ in an amount from 5.0 to 10.0% by weight; La₂O₃ in an amount from 10.0 to 26.0% by weight; Nb₂O₅ in an amount from 0.0 to 2.0% by weight; and TiO₂ in an amount from 0.0 to 1.5% by weight.
 17. The composite product of claim 12, wherein said composition is substantially free of fluorine and lead.
 18. The composite product of claim 12, wherein said polymer matrix is polymer selected from the group consisting of polyesters, polypropylene, polyamide, polyethylene terephtalate, polybutylene, epoxy resins, unsaturated polyesters, phenolics, vinylesters and combinations thereof.
 19. A method of Raining glass fibers having a high refractive index comprising: providing a molten glass composition including: SiO₂ in an amount from 30.0 to 40.0% by weight; Al₂O₃ in an amount from 15.0 to 23.0% by weight; Y₂O₃ in an amount from 15.0 to 35.0% by weight; B₂O₃ in an amount from 0.0 to 15.0% by weight; K₂O in an amount from 0.0 to 5.0% by weight; La₂O₃ in an amount from 0.0 to 30.0% by weight; Li₂O in an amount from 0.0 to 3.0% by weight; Na₂O in an amount from 0.0 to 4.0% by weight; Nb₂O₅ in an amount from 0.0 to 10.0% by weight; TiO₂ in an amount from 0.0 to 7.5% by weight; WO₃ in an amount from 0.0 to 10.0% by weight; and RO in an amount from 0.0 to 7.5% by weight, wherein RO is one or more of MgO, CaO, SrO, and BaO; and drawing said molten glass composition through orifices in a bushing to form a glass fiber having a refractive index between about 1.55 and about 1.69.
 20. The method of claim 19, wherein said glass fiber has an Abbe number less than about
 65. 21. The method of claim 20, wherein said composition is substantially free of fluorine and lead.
 22. The method of claim 21, wherein said glass fiber has a coefficient of thermal expansion less than about 66×10⁻⁷ cm/cm. 